Title: Europium-doped Ba7F12Cl2, a single component near-UV excited tunable white phosphor
Authors : Hagemann, Hans
Bill, Hans
Rey, Julien
Kubel, Frank
Calame, Laurent
Lovy, Dominique
Published in : The journal of physical chemistry. C
Volume(Issue) : 119
Issue : 1
Pages : 141
Pages to: 147
Publisher / Ed. Institution : American Chemical Society
Issue Date: 2014
License (according to publishing contract) : Licence according to publishing contract
Type of review: Peer review (Publication)
Language : English
Subject (DDC) : 540: Chemistry
Abstract: Europium-doped crystalline Ba7F12Cl2 phosphors have been prepared at temperatures between 650 and 900 °C using alkali chloride fluxes, yielding both disordered (with the incorporation of small amounts of Na) and ordered crystal modifications. The white emission spectrum excited in the near UV consists roughly of two broad emission bands at about 450 and 590 nm, as well as weak sharp Eu2+ 4f–4f emission bands around 360 nm. The incorporation of Eu2+ is further studied using EPR spectroscopy on single crystals and reveals a significant zero field splitting. The emission spectrum can be significantly tuned by varying the excitation wavelength between 300 and 390 nm. Fine tuning may also be achieved by chemical substitutions to form Ba7–xMyF12Cl2–zBrz (M = Na, Ca, Eu). Quantitative measurements of the light produced using commercial near UV LEDs show that the color temperature ranges between 4000 and 9700 K with CIE chromaticity coordinates close to the ideal values of x = y = 0.333. The best color rendering index (CRI) found was 0.83 and the highest light to light conversion yield was 171 lm/W. These results show that the title compound is a very promising candidate for white light generation using near UV LED excitation.
Departement: School of Engineering
Organisational Unit: Institute of Applied Mathematics and Physics (IAMP)
Publication type: Article in scientific Journal
DOI : 10.1021/jp510301p
ISSN: 1932-7447
1932-7455
URI: https://digitalcollection.zhaw.ch/handle/11475/15841
Appears in Collections:Publikationen School of Engineering

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.